A. M. Zahedi, H. R. Rezaie, J. Javadpour,
Volume 12, Issue 4 (12-2015)
Abstract
Different volume fractions (1.3, 2.6, and 7.6 Vol.%) of carbon nanotubes (CNTs) were dispersed within 8Y-TZP nanopowders. Mixed powder specimens were subsequently processed by spark plasma sintering (SPS) and effects of CNTs on the sintering process of 8Y-TZP/CNT composites was studied. Maintenance of CNTs through the SPS process was confirmed using TEM and Raman Spectroscopy. Studies on the sintering profile of zirconia-CNT composites (Z-xC composites) could, to some extent, clarify the effect of CNTs’ volume fraction on the densification rates of Z-xC composites. The specimen with the highest content of CNT (Z-7.6C) showed the lowest sintering rate while it was unable to reach full density.
![\"AWT](\"./files/site1/images/qqq.png\")
S. Ghasemi-Kahrizsangi, H. Gheisari-Dehsheikh, M. Boroujerdnia,
Volume 13, Issue 4 (12-2016)
Abstract
In this study the effect of nano meter size ZrO2 particles on the microstructure, densification and hydration resistance of magnesite –dolomite refractories was investigated. 0, 2, 4, 6 and 8 wt. % ZrO2 particles that were added to magnesite –dolomite refractories containing 35 wt. % CaO. The Hydration resistance was measured by change in the weight of specimens after 72 h at 25℃ and 95% relative humidity. The results showed with addition of nano meter size ZrO2 particles, the lattice constant of CaO increased, and the bulk density and hydration resistance of the specimens increased while apparent porosity decreased. With the addition of small amount ZrO2 the formation of CaZrO3 phase facilitated the sintering and the densification process. The mechanism of the nano meter size ZrO2 particles promoting densification and hydration resistance is decreasing the amount of free CaO in the specimens.
Farzaneh Sadat Teimoory Toufal, Alma Kalali, Arvin Attari Navab, Mohadeseh Reyhani, Hamidreza Rezaie, Jafar Javadpour,
Volume 21, Issue 0 (3-2024)
Abstract
Glass ionomer cements (GICs) are widely utilized in clinical restorative dental applications, which suffer from poor mechanical strength. Recent research shows that GIC achieves optimal performance when modified with lower percentage of filler materials, particularly when using nanoparticles, due to the resultant increase in surface area and packing density of the cement. Notably, while some modifications show promise, others fail to deliver improvements in material characteristics. This study addressed a gap in the literature by investigating the impact of acidic/basic additives, such as Diopside (CaMgSi2O6) and Zirconia (ZrO2), on the properties of the cement. The reactivity of zirconia and Diopside differ distinctly from traditional calcium-aluminosilicate glass when exposed to acidic conditions in GICs. Also, to clarify the impact of acidity/basicity on filler reactivity during cement setting, the potential mechanical enhancement effects by using nano-sized particles is limited to submicrons. This research incorporated Diopside at concentrations of 2, 4, and 6 wt.%, and zirconia at 8, 10, and 12 wt.% into a glass powder component. Results demonstrated that adding 8 wt.% Zirconia led to a 49% enhancement in compressive strength, also improve microhardness by 16 wt.%, attributed to its non-reactive nature, minimal dissolution, and high inherent strength of ZrO2. In contrast, Diopside had a detrimental effect due to its basic nature compared to that of glass powder. These findings highlight the potential of zirconia as a valuable reinforcing material for the successful mechanical performance of glass ionomer cements. Conversely, basic fillers like diopside appear unsuitable for achieving improved mechanical performance in these systems.